Advancing PLA 3D Printing with Laser Polishing: Improving Mechanical Strength, Sustainability, and Surface Quality

Three-dimensional (3D) printing of polylactic acid using the fused filament fabrication approach is a widely used additive manufacturing method in various fields, despite the historical issue of substantial surface roughness in fused filament fabrication products. Several strategies have been utilized to minimize the surface roughness of 3D-printed items. However, laser polishing is a novel technique for reducing surface roughness and improving other material qualities. In this study, polylactic acid was examined using the laser polishing method for surface roughness and mechanical properties, such as tensile and flexural strength and laser scan time. Several trials were conducted to determine how changing the laser’s characteristics may affect the materials’ surface quality and mechanical qualities. Before the final test, preliminary tests were performed to determine the lowest potential heat-affected zone. Laser polishing reduced surface roughness by more than 88.8% (from 7.8 µm to 0.87 µm). The tensile strength of the specimen increased by 14.03%, from 39.2 MPa to 44.7 MPa. Polylactic acid had a constant flexural strength of 70.1 MPa before and after polishing, and the laser scan time for samples was 19.4 s. Polished morphologies were studied to learn more about the microstructure. These findings show that laser polishing can improve and modify the surface properties of a fused filament fabrication product, which can benefit the industry and researchers.