Temperature Stable, High-Quality Factor Li2TiO3-Li4NbO4F Microwave Dielectric Ceramics

In this work, (1-x)Li2TiO3-xLi4NbO4F ceramics were prepared by the conventional solid-state ceramic route. With the increase of Li4NbO4F content, the phase structure transformed from ordered monoclinic to disordered cubic. By increasing Li3NbO4F content, the temperature coefficient of resonant frequency (τf) was successfully adjusted closer to zero, while the dielectric constant (εr) and microwave quality factor (Qf) decreased to some degree. Outstanding microwave dielectric properties with a εr = 18.7, Qf = 61,388 GHz (6.264 GHz), and τf = 0.9 ppm/°C were obtained for 0.9Li2TiO3-0.1Li4NbO4F ceramics sintered at 1050 °C for 2 h, which indicated that these ceramics are suitable for practical applications in the field of microwave substrates and components.