Sequential ion irradiations on Fe-Cr and ODS Fe-Cr alloys

Oxide dispersion strengthened steels are candidate materials for nuclear reactor applications due to a powerful combination of properties, such as reduced activation, high-temperature strength and increased creep resistance. The dispersion of nanometric oxide particles in the steel matrix may also enhance radiation resistance by acting as trapping sites for irradiation induced defects. In this work, an Fe–14Cr–2 W–0.3-Ti–0.3Y2O3 (wt%) steel and a model Fe-14Cr (wt%) alloy were sequentially irradiated with He+ and Fe+ ions up to 15 dpa and 8000 appm to simulate fusion radiation damage. Their microstructural stability was investigated by positron annihilation spectroscopy and transmission electron microscopy. Transmission electron microscopy studies show that under these irradiation conditions there are no significant changes in the mean size, qualitative chemical composition and number density of nanoparticles, although the irradiation appears to induce a slight coarsening of the smaller nanoparticles. Both materials exhibit very small (