Mechanical Properties and Mesoscopic Numerical Simulation of Local Weakening in High-Performance Concrete after 10 Years of Alkali Solution Immersion

The natural environment in the high-altitude regions of Northwest China is extremely harsh, characterized by numerous salt lakes. The high concentrations of chloride salts, sulfates, and alkali metal ions in these areas can induce alkali–silica reactions (ASRs) in concrete. These reactions generate harmful gel within the concrete, causing expansion and cracking, which significantly impacts the durability of concrete structures. This study investigates the evolution of the mechanical properties in high-performance concrete (HPC) under long-term ASR by incorporating different admixtures and varying the equivalent alkali content. A three-dimensional random aggregate mesoscopic model was used to simulate static compression tests under various operational conditions. Non-destructive testing methods were utilized to determine the expansion rate, internal, and surface damage variables of the concrete. The experimental results indicate that the 10-year expansion rate differs from the 1-year rate by approximately 1%, and under long-term ASR mitigation measures, the internal damage in the HPC is minimal, though the surface damage is more severe. As the equivalent alkali content increases, the compressive strength of the concrete cubes decreases, initially rising before falling by 5–15% over time. The HPC with only air-entraining agent added exhibited better mechanical performance than the HPC with both air-entraining and corrosion inhibitors added, with the poorest performance observed in the HPC with only a corrosion inhibitor. A relationship was established between the surface and internal damage variables, with the surface damage initially increasing rapidly before stabilizing as the internal damage rose. Numerical simulations effectively describe the damage behavior of HPC under static uniaxial compression. Comparisons with actual failure morphologies revealed that, in the cube compression tests, crack propagation directly penetrated both coarse and fine aggregates rather than circumventing them. The simulations closely matched the experimental outcomes, demonstrating their accuracy in modeling experiments. This study discusses the compressive mechanical properties of concrete under prolonged ASR through a combination of experimental and simulation approaches. It also delves into the impact of surface damage on the overall mechanical performance and failure modes of concrete. The findings provide experimental and simulation support for the concrete structures in regions with high alkali contents.