Pt3Ni@C Composite Material Designed and Prepared Based on Volcanic Catalytic Curve and Its High-Performance Static Lithium Polysulfide Semiliquid Battery

There are many challenges for the Static lithium polysulfide semiliquid battery in its commercial application, such as poor stability of the cathode material and further amplification of the lithium polysulfide shuttle effect. Therefore, this manuscript introduced a new type of Pt3Ni@C composite material as cathode working electrode based on the principle of volcanic catalytic curve. Through symmetric battery test, CV, polarization curves and impedance test, it was found that Pt3Ni@C composite material had good catalytic activity of lithium polysulfide to improve electrochemical kinetics. When the catholyte was Li2S8 and the charge-discharge voltage range was 1.8~2.6 V, the capacity maintained at approximately 550 mAh g−1, and the coulombic efficiency maintained at approximately 95% after 100 cycles at a current rate of 0.5 mA cm−2. The Pt3Ni@C composite material is a potential cathode material with the specific capacity and long cycling stability of the static lithium polysulfide semiliquid battery.