Effect of Microstructure on the Compressive Mechanical Properties of Ti-20Zr-6.5Al-4V Alloy

The effect of microstructure on the mechanical properties of Ti-20Zr-6.5Al-4V alloy after solution and aging treatment was investigated by compression tests. The results showed that the microstructure was consisted of a duplex phase αʺ + β structure after solution treatment. With increasing solution treatment temperature, the size of β phase grain increased and the amount of αʺ phase decreased. The ultimate compressive strength and elongation decreased with increasing solution treatment temperature, while the yield strength increased. After aging-treatment at 700 ºC for 1.5 h, the microstructure consisted of a large amount of globular α phase, a little amount of fine acicular α phase and bulk β phase for the samples solution-treated at 850 ºC for 0.5 h. With increasing initial solution treatment temperature, the amount of globular α phase and bulk β phase decreased, however, the amount and size of acicular α phase increased after aging treatment. The ultimate compressive strength and elongation decreased with increasing initial solution treatment temperature, whereas the yield strength firstly increased, and then slightly decreased.