Effects of TiO2 addition on phase, mechanical properties, and microstructure of Cr2O3–Al2O3 ceramic composite

TiO2 is a sintering additive that can significantly improve the sintering and mechanical properties of Cr2O3–Al2O3 refractory materials with high Cr2O3 contents. In this study, TiO2-reinforced Cr2O3–Al2O3 composite refractories were prepared using a reaction-sintering process. The microstructure, phase composition, mechanical properties, and strengthening mechanism of the TiO2-reinforced Cr2O3–Al2O3 composite refractories were investigated. The results indicated that the Al2O3–Cr2O3–TiO2 composite refractory with a TiO2 content of 3.0–4.5 wt% had good compactness (porosity of 5.89%), hardness (17.21 GPa), wear resistance (wear rate of 0.4 mm3/Nm), flexural strength (101.10 MPa), and compressive strength (420.90 MPa). This is mainly because when the added amount of TiO2 was