Comportamiento plástico a alta temperatura de Al2O3 codopado con CuO y TiO2 fabricado por reacción

The high temperature plastic behavior of reaction-bonded alumina doped with equimolar amounts of copper and titanium oxides (CuO and TiO2, respectively) has been studied by means of creep and stress relaxation tests in air. Deformation results have been correlated with microstructural observations and X-ray diffraction studies in order to deduce the mechanism responsible for the deformation. This material exhibits plasticity at temperatures as low as 950ºC in contrast with other aluminas. At temperatures near 1000ºC a linear relation between the strain rate and the stress has been detected (a stress exponent n equal to 1) but both above and below this temperature higher values of n have been observed.Se ha estudiado el comportamiento plástico a alta temperatura de alúmina codopada con cantidades equimolares de óxidos de cobre (CuO) y titanio (TiO2) fabricada por reacción mediante el empleo de ensayos de fluencia y de relajación de tensiones en atmósfera de aire. Los resultados de los ensayos de deformación plástica han sido correlacionados con observaciones microestructurales y difracción de rayos X con vistas a deducir el mecanismo responsable del proceso de deformación. Este material presenta comportamiento plástico a temperaturas tan bajas como 950ºC en contraste con otras aluminas. A temperaturas alrededor de 1000ºC se ha observado una relación lineal entre la velocidad de deformación y la tensión (exponente de tensión igual a uno) mientras que a temperaturas por encima y por debajo de este valor el exponente de tensión toma valores más elevados.