Inserción electroquímica de litio en la solución sólida Nb8-nW9+nO47 (1≤ n ≤6)

Electrochemical lithium insertion have been carried out in different compostions within the solid solution with general formula Nb8-nW9+nO47 (1≤ n ≤6). Through galvanostatic and potentiostatic techniques we have detected that lithium insertion proceeds by at least two reduction step. These process seem are relationship with the molar ratio Nb/W. The maximum lithium content reached leads to a specific capacity of 170 Ah/kg. Nevertheless, due to irreversible structural transformations in the matrix-host such capacity was lost after the first cycle. The detailed analysis about the insertion kinetic process and in situ X-ray diffraction experiments have been carried out in this work.A través de diferentes técnicas electroquímicas hemos realizado el estudio de la inserción de litio en una serie de composiciones pertenecientes a la solución sólida Nb8-nW9+nO47 (1≤ n ≤6). La inserción de litio procede al menos a través de dos procesos de reducción, los cuales guardan cierta relación con el contenido de Nb/W. La máxima cantidad de litio insertada conduce a capacidades específicas de la celda del orden de los 170 Ah/kg, la cual se pierde en sucesivos procesos de carga-descarga. Igualmente, hemos realizado un análisis de la cinética de los procesos de reducción y de los cambios estructurales que se suceden en la estructura del óxido de partida a medida que se inserta el litio a través de la difracción de rayos-X in situ.