Influence of Preheating Self-Adhesive Cements on the Degree of Conversion, Cell Migration, and Cell Viability

Enhancing the degree of polymerization can mitigate the cytotoxic effects of resinous materials, as residual monomers have been identified as a significant contributor to cytotoxicity. Hence, the aim of the current research was to evaluate the influence of preheating self-adhesive cements at 39 °C on cell migration, cytotoxicity, and degree of conversion. RelyX U200, Set PP, and MaxCem Elite were subjected to Fourier Transform Infrared Spectroscopy–Attenuated Total Reflection (FTIR–ATR). Self-adhesive resin cements were applied onto an ATR device, with samples subjected to either heated or room temperature conditions, followed by photoactivation. For the cytotoxicity analysis, extracts (24 h and 7 days) were placed in contact with NIH/3T3 cells. For cell migration, images were captured of each sample until the possible closure of the cleft occurred. A two-way analysis of variance (ANOVA) was conducted to assess the effect of preheating on the degree of conversion and cell viability within the self-adhesive cements tested. A significance level of 5% was set for statistical purposes. In the results of the degree of conversion, preheating did not improve the conversion of cements (p > 0.05). For the 3-(4-5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT), preheating did not improve the results within 24 h, however, it generated positive results within 7 days for the Set PP resin cement (p < 0.05). For cell migration, high rates of cell death were found in all groups. It is concluded that preheating at 39 °C causes a positive effect only in increasing the cell viability of the Set PP resin cement and that both materials analyzed are highly cytotoxic.