Analysis of color stability and degree of conversion of different types of resin composites

Abstract Resin composites containing surface pre-reacted glass (S-PRG) have been introduced to reduce demineralization and improve remineralization of the tooth structure. However, water diffusion within the material is necessary for its action, which can impair its overall physicomechanical properties over time, including color stability. This study aimed to evaluate the color stability and related degree of conversion (DC) of four resin composites. Discs (6 x 4 mm, n = 5/group) of microhybrid (MH), nanofilled (NF), nanohybrid (NH), and S-PRG-based nanohybrid (S-PRG-NH) composites with two opacities (A2/A2E and A2O/A2D) were prepared. Color (CIELab and CIEDE2000) was evaluated with a spectrophotometer after aging in grape juice (2 x 10 min/10mL/7days). The DC was analyzed by using Fourier transform infrared spectroscopy before and after light-curing. Data were statistically analyzed by using two-way analysis of variance and post-hoc least significant difference tests (p