Wear Properties of Sc-Bearing Zr-Based Composite BMG with Nano-CuZr2 under Lubrication

Lubricated sliding wear of amorphous (Zr55Cu30Ni10Al5)99.98Sc0.02/CuZr2 nanocrystal composite bulk metallic glasses (BMG) under various sliding velocities with a load of 20 N was investigated using the pin-on-disk test. After the wear test involving oil lubrication was performed, there was no wear induced new-phase transformation in the sample surface. Friction coefficients were within the range from 0.22 to approximately 0.29 under a 20-N load at different sliding velocities. Therefore, the calculated friction coefficients clearly indicated that the adhesion wear dominated from the experimental results. This deformation behavior resulted in a higher wear rate and wear coefficient. In addition, worn surfaces were characterized and examined under a scanning electron microscope (SEM) and optical microscope. The mechanism of high wear rate was clarified.