Analysis on High Temperature Aging Property of Self-brazing Aluminum Honeycomb Core at Middle Temperature
- Source :
- Cailiao gongcheng, Vol 44, Iss 11, Pp 39-44 (2016)
- Publication Year :
- 2016
- Publisher :
- Journal of Materials Engineering, 2016.
-
Abstract
- Tension-shear test was carried out on middle temperature self-brazing aluminum honeycomb cores after high temperature aging by micro mechanical test system, and the microstructure and component of the joints were observed and analyzed using scanning electron microscopy and energy dispersive spectroscopy to study the relationship between brazing seam microstructure, component and high temperature aging properties. Results show that the tensile-shear strength of aluminum honeycomb core joints brazed by 1060 aluminum foil and aluminum composite brazing plate after high temperature aging(200℃/12h, 200℃/24h, 200℃/36h) is similar to that of as-welded joints, and the weak part of the joint is the base metal which is near the brazing joint. The observation and analysis of the aluminum honeycomb core microstructure and component show that the component of Zn, Sn at brazing seam is not much affected and no compound phase formed after high temperature aging; therefore, the main reason for good high temperature aging performance of self-brazing aluminum honeycomb core is that no obvious change of brazing seam microstructure and component occurs.
Details
- Language :
- Chinese
- ISSN :
- 10014381
- Volume :
- 44
- Issue :
- 11
- Database :
- Directory of Open Access Journals
- Journal :
- Cailiao gongcheng
- Publication Type :
- Academic Journal
- Accession number :
- edsdoj.016ecd3fd94d70b2454bf64ee185d2
- Document Type :
- article
- Full Text :
- https://doi.org/10.11868/j.issn.1001-4381.2016.11.006