Синтез вуглець-кремнеземних наноматеріалів карбонізацією сополімеру ацетату целюлози з поліізоціанатом

Cellulose acetate and polyisocyanate copolymer synthesized by mechanical mixing of cellulose acetate, polyisocyanate and fumed silicon dioxide in the presence of nickel chloride was carbonized in silicon dioxide template. Copolymer and silicon dioxide template were formed simultaneously. Composite structure and composition was studied with SEM and EDS. SEM showed that porous carbonaceous nanomaterial was synthesized. Formed carbon is represented by coating on silicon dioxide, layered ribbon-like and fibrous structures in template pores with size from several nm (thickness) to several microns (length). Metallic nickel crystals up to 200 nm in size were fabricated in composite pores from Nickel chloride by reduction of Ni2 with products of pyrolysis of organic compounds. Key words: carbon-silica nanomaterials, polyisocyanate, cellulosr acetate, fumed silica, nickel chloride, carbonization.
Карбонізацією сополімеру ацетату целюлози з поліізоціанатом в матриці із силіцій діоксиду синтезовано вуглець-кремнеземний наноматеріал, який складається із наночасток SiO2 та вуглецевих наноутворень розміром від декількох нм (товщина) до декількох мкм (довжина). Структуру і склад піровуглецю досліджували методами СЕМ та ЕДРС. В присутності у реакційній суміші нікол хлориду в порах композиту додатково до вуглецевого покриття на частинках SiO2 утворюються шарувато-стрічкові та волокнисті наноструктурі вуглецю розміром до декількох мкм та частинки металевого Ніколу розміром до 200 нм. Ключові слова: вуглець-кремнеземні наноматеріали, поліізоціанат, ацетат целюлози, пірогенній кремнезем, нікол хлорид, карбонізація.