МАТЕМАТИЧНЕ МОДЕЛЮВАННЯ СТРУКТУРОУТВОРЕННЯ ПРИ НАПЛАВЛЕННІ ВІДНОВЛЮВАЛЬНИХ ПОКРИТТІВ З ВИКОРИСТАННЯМ МОДИФІКУЮЧОЇ ДОМІШКИ БЕНТОНІТОВОЇ ГЛИНИ

The coating process has a decisive influence on the structural and phase transformations in the coating. A wide change in the chemical composition of the deposited layer depends on the share of the main and filler materials, high heating temperature in the range of cooling rates. This leads to the formation of different structural-phase states in the surface layer made of the same surfacing material. The aim of this work was to model the structure using an optical-mathematical description of its variability with the introduction of a modifying clay impurity. An optical-mathematical description of its variability during the introduction of a modifying clay impurity into the restorative coating during surfacing on a thin-walled cultivator paw of agricultural machinery was used to model the formation. The studies were based on a comparative analysis of the basic variant of surfacing and with the introduction of a modifying impurity. For the first time, a natural modifying impurity, clay, was used to modify the liquid bath of the reinforcing coating and the analysis of structural changes in the coating was performed by optical-mathematical description of the phases and their fraction relative to the initial state. To do this, the color histograms of the photographs were compared according to Kolmogorov's criterion. Analyzed statistical results on 15 intervals of the formed phases. In this embodiment, the carbon electrode was used to weld the coating to clearly detect the effect of the modifying impurity. The comparison showed great homogeneity in the phase distribution when modified with bentonite clay. The obtained images in the photographs fully reflect the structure formation when modifying the coatings, where it is possible to trace not only the shape and distribution of the hardest carbide phase, but also to estimate the number and interaction of all structural components. Studies have shown that additional modification with bentonite clay with a share of 5—7% of the electrode fraction increases the ferrite component by 2.4%, carbides by 32%, reduces bainite by 5.4%, and changes the phase interaction, which reduces the size grains, stresses in the transition zone.
Використана методика оптико-математичного моделюванням структуроутворення наплавлювальних покриттів з використанням в якості модифікуючої домішки бентонітової глини. Порівняння варіантів наплавлення показало велику однорідність у розподілі фаз при модифікуванні бентонітової глиною. Отримані оброблені зображення на фотографіях в повній мірі відображають структуроутворення при модифікуванні покриттів, де можна простежити не тільки форму і розподіл найбільш твердої фази карбіду, а й оцінити кількість і взаємодію всіх структурних складових.