Samosíťující latexy se zvýšenou tepelnou stabilitou

In this contribution the application of a novel flame retardant based on halogenophosphazene derivative in waterborne coatings based on self-crosslinking latexes was investigated. Hexaallylamino-cyclo-triphosphazene was synthesized by nucleophilic substitution of hexachloro-cyclo-triphosphazene with allyl amine. Latexes of functionalized core-shell particles bearing in the structure a covalently linked hexachloro-cyclo-triphosphazene were prepared by the semi-continuous non-seeded emulsion polymerization of methyl methacrylate, butyl acrylate and methacrylic acid as main monomers. For interfacial crosslinking, diacetone acrylamide was copolymerized into the shell layer of latex particles to provide sites for subsequent reaction with adipic acid dihydrazide. The incorporation hexaallylamino-cyclo-triphosphazene did not affect transparency, flexibility, toughness and adhesive properties of resulting coatings. Moreover, the presence of the novel flame retardant increased the flame stability of coatings. Tento příspěvek pojednává o využití nového retardéru hoření na bázi derivátu halogenofosfazenu ve vodouředitelných nátěrech založených na samosíťujících latexech. Hexaalllyamino-cyklo-trifosfazen byl syntetizován nukleofilní substitucí hexachloro-cyklo-trifosfazenu allylaminem. Semikontinuální emulzní polymerací methylmethakrylátu, butylakrylátu a kyseliny methakrylové byly připraveny latexy tvořené funkcionalizovanými core-shell částicemi nesoucími kovalentně zapojený hexachloro-cyklo-trifosfazen. Diacetonakrylamid byl kopolymerován v obalové vrstvě latexových částic, aby byla zajištěna reaktivní místa pro post-síťování pomocí dihydrazidu kyseliny adipové. Zabudování hexaalllyamino-cyklo-trifosfazenu neovlivnilo transparentnost, pružnost, houževnatost ani adhezní vlastnosti výsledných nátěrů. Přítomnost nového retardéru hoření navíc zvýšila tepelnou odolnost nátěrů.