Dielectric and ultrasonic studies of new Ag0.1Cu0.9InP2S6 layered ferroelectric compound

The dielectric properties of newly synthesized Ag0.1Cu0.9InP2S6 crystals were investigated in broad frequency (20 Hz – 1 MHz) and temperature range (110 K – 350 K). Anomaly in the temperature dependence of a complex dielectric permittivity indicating the polar phase transition was detected at the temperature 283 K. The dielectric properties of the presented crystal are mainly caused by conductivity and phase transition. The frequency spectra of the conductivity obey the Almond-West power law. The activation energy of the conductivity was found to be EA/k= 6381 K. A suggestion is given that the electric conductivity in these crystals can be interpreted by ionic mechanism. The piezoelectric sensitivity was observed only when DC bias electric field was applied along direction normal to layers. In this case the piezoelectric sensitivity appeared due to electrostriction. Ištirtos dielektrinės ir ultragarsinės Ag0,1Cu0,9InP2S6 kristalo savybės. Dielektrinės skvarbos spektrai buvo matuojami žemųjų (20-106 Hz) srityse. Matuota kristalą šaldant nuo 350 K iki 110 K temperatūros. Kompleksinės dielektrinės skvarbos ε* realiosios ir menamosios dalių priklausomybės nuo temperatūros parodo, kad kristale reiškiasi dielektrinė dispersija – dielektrinės skvarbos priklausomybė nuo elektrinio lauko kitimo dažnio. Tiek iš realiosios, tiek iš menamosios dielektrinės skvarbos temperatūrinių priklausomybių galima išskirti dvi būdingąsias sritis: joninio laidumo ir fazinio virsmo sąlygotas dielektrinės skvarbos dispersijas. Žemojo dažnio srityje ir aukštoje temperatūroje (T > 290 K) dispersiją sąlygoja tūrinis kristalo laidumas. Dėl fazinio virsmo atsirandanti dispersija matyti visoje matuotų dažnių srityje ir temperatūroje, artimoje fazinio virsmo temperatūrai (T ≈ 283 K).