Core/shell fibers of Carboxymethylcellulose/ Poly(lactic acid) loaded with Curcumin

Resumen Para dosificar curcumina (Cur) evitando su degradación, se diseñó un material polimérico que consta de fibras con estructura núcleo/coraza. Se utilizó la técnica de electrohilado coaxial para obtener de fibras con núcleo de ácido poliláctico (PLA) y coraza de carboximetilcelulosa (CMC). Fibras de CMC/PLA fueron comparadas con fibras convencionales de PLA cargadas con curcumina. Imágenes de microscopia electrónica de barrido permitieron caracterizar la estructura núcleo/coraza de las fibras de CMC/PLA-Cur. La presencia de Cur en las fibras fue confirmada por espectroscopia Raman. Análisis termogravimétrico y calorimetría diferencial de barrido mostraron el efecto de la incorporación de Cur en el comportamiento térmico y permitió contrastar las fibras de PLA con las de CMC/PLA. Se realizaron experimentos de liberación de Cur a pH fisiológico y los resultados se ajustaron al modelo de Korsmeyer-Peppas. La tasa de liberación de fibras de CMC/PLA es significativamente menor a la de fibras de PLA sin coraza. Abstract To dose curcumin (Cur) while avoiding its degradation, a polymeric material consisting of fibers with core/ shell structure was designed. Coaxial electrospinning allowed us to obtain fibers with poly(lactic acid) (PLA) core, and carboxymethylcellulose (CMC) shell. CMC/PLA fibers were compared with conventional PLA fibers. Scanning electron microscopy images allowed us to characterize the core/shell structure of CMC/ PLA-Cur fibers. The presence of Cur in the fibers was confirmed by Raman spectroscopy. Thermogravimetric analysis and differential scanning calorimetry showed the effect of Cur on the thermal behavior of the fibers, and showed contrasting behavior between CMC/PLA and PLA fibers. Cur release experiments were performed at physiological pH and the results were fitted with the Korsmeyer-Peppas model. The release rate of CMC/PLA fibers was significantly lower than PLA fibers.