Análise da redução do consumo de cimento Portland por meio da utilização de nanotubos de carbono de paredes múltiplas funcionalizados em argamassa

The use of carbon nanotubes in cementitious materials improves the mechanical properties of these composites and increases their compressive and flexural strength. The main objective of this study was to evaluate the technical feasibility of reducing the Portland cement content by using functionalized multi-walled carbon nanotubes (MWCNT) in mortar samples, using mechanical properties as parameters (compressive strength, flexural strength and modulus of elasticity). Experimental results allowed us to conclude that the addition of MWCNT in 0.1% by weight of Portland cement, to the mortar samples allowed a reduction of the Portland cement content by up to 10%, while the water/cement ratio remained unchanged without affecting the mechanical behavior. Resumo A utilização de nanotubos de carbono em materiais cimentícios melhora as propriedades mecânicas destes compósitos, aumentando a sua resistência à compressão e à flexão. O principal objetivo deste estudo foi avaliar a viabilidade técnica da redução do teor de cimento Portland através da utilização de nanotubos de carbono de paredes múltiplas funcionalizados (MWCNT) em amostras de argamassa, utilizando como parâmetros as propriedades mecânicas (resistência à compressão, resistência à flexão e módulo de elasticidade). Os resultados experimentais permitiram concluir que a adição de MWCNT em 0,1% em peso de cimento Portland, às amostras de argamassa, permitiu uma redução do teor de cimento Portland em até 10%, mantendo-se inalterada a relação água/cimento, sem afetar o comportamento mecânico.