Avaliação in vitro da citotoxicidade e atividade antimicrobiana em biofilme de diferentes cimentos endodônticos obturadores

Objective: Evaluate the cytotoxicity in human osteoblastic cells and antimicrobial activity in different root canal sealers in vitro. Methods: BioRoot RCS, TotalFill BC Sealer, and Bio-C Sealer were used in experimental groups, and AH Plus was used as a control. Human osteoblast-like cells and MTT quantitative colorimetric assay were used to evaluate cytotoxicity. Saos-2 cells were exposed to undiluted sealer extracts for 24 h. The supernatant was then collected and the formazan crystals resulting from MTT reduction were dissolved in pure dimethyl sulfoxide. Absorbance was measured in an automated spectrophotometer at a wavelength of 540 nm. Antimicrobial activity was analyzed by the direct contact test using a polymicrobial biofilm composed of Enterococcus faecalis, Candida albicans, and Streptococcus mutans. At 24, 48, and 72 h, colony-forming units were counted on agar plates. A nonparametric Kruskal-Wallis test was used for the statistical analysis. The level of significance was set at 5%. Results: AH Plus showed the lowest cytotoxicity after 24 h, with a significant difference in relation to BioRoot RCS and Bio-C Sealer (p ≤ 0.01). There was no significant difference in cytotoxicity between TotalFill BC Sealer and Bio-C Sealer (p > 0.05). At 24 h, TotalFill BC Sealer and AH Plus showed the least microbial growth compared to Bio-C Sealer (p 0.05). Conclusions: AH Plus had the lowest cytotoxicity. TotalFill BC Sealer and AH Plus yielded greater reductions in microbial counts in the first 24 h compared to Bio-C Sealer. Clinical Relevance: 2c. Objetivo: Evaluar in vitro la citotoxicidad en células osteoblásticas humanas y la actividad antimicrobiana de diferentes cementos obturadores de conductos radiculares. Materiales y métodos: BioRoot RCS, TotalFill BC Sealer y Bio-C Sealer se utilizaron como grupos experimentales y AH Plus se utilizó como control. Se usaron células similares a osteoblastos humanos y ensayo colorimétrico cuantitativo MTT para evaluar la citotoxicidad. Las células Saos-2 se expusieron a extractos de cementos sin diluir durante 24 h. A continuación, se recogió el sobrenadante y los cristales de formazán resultantes de la reducción de MTT se disolvieron en sulfóxido de dimetilo puro. La absorbancia se midió en un espectrofotómetro automático con una longitud de onda de 540 nm. La actividad antimicrobiana se analizó mediante la prueba de contacto directo, utilizando una biopelícula polimicrobiana compuesta por Enterococcus faecalis, Candida albicans y Streptococcus mutans. A las 24, 48 y 72 h, se contabilizaron las unidades formadoras de colonias en placas de agar. Para el análisis estadístico se utilizó la prueba no paramétrica de Kruskal-Wallis. El nivel de significación se fijó en el 5%. Resultados: AH Plus mostró la menor citotoxicidad después de 24 h, con una diferencia significativa en relación con BioRoot RCS y Bio-C Sealer (p ≤ 0.01). No hubo diferencias significativas en la citotoxicidad entre TotalFill BC Sealer y Bio-C Sealer (p > 0.05). A las 24 h, TotalFill BC Sealer y AH Plus mostraron el menor crecimiento microbiano en comparación con Bio-C Sealer (p 0.05). Conclusiones: AH Plus presentó la menor citotoxicidad. TotalFill BC Sealer y AH Plus produjeron mayores reducciones en los recuentos microbianos en las primeras 24 h en comparación con Bio-C Sealer. Relevancia Clínica: 2c. Objetivo: Avaliar a citotoxicidade em células osteoblásticas humanas e a atividade antimicrobiana em diferentes cimentos endodônticos in vitro. Métodos: BioRoot RCS, TotalFill BC Sealer e Bio-C Sealer foram usados nos grupos experimentais e o AH Plus foi usado como controle. Células semelhantes a osteoblastos humanos e ensaio colorimétrico quantitativo de MTT foram usados para avaliar a citotoxicidade. As células Saos-2 foram expostas a extratos de cimento não diluídos por 24 h. O sobrenadante foi então recolhido e os cristais de formazan resultantes da redução do MTT foram dissolvidos em dimetilsulfóxido puro. A absorbância foi medida em um espectrofotômetro automatizado em um comprimento de onda de 540 nm. A atividade antimicrobiana foi analisada pelo teste de contato direto utilizando um biofilme polimicrobiano composto por Enterococcus faecalis, Candida albicans e Streptococcus mutans. Em 24, 48 e 72 h, as unidades formadoras de colônias foram contadas em placas de ágar. O teste não paramétrico de Kruskal-Wallis foi utilizado para a análise estatística. O nível de significância foi estabelecido em 5%. Resultados: AH Plus apresentou a menor citotoxicidade após 24 h, com diferença significativa em relação ao BioRoot RCS e Bio-C Sealer (p ≤ 0,01). Não houve diferença significativa na citotoxicidade entre TotalFill BC Sealer e Bio-C Sealer (p > 0,05). Às 24 h, TotalFill BC Sealer e AH Plus apresentaram o menor crescimento microbiano em comparação com Bio-C Sealer (p 0,05). Conclusões: AH Plus apresentou a menor citotoxicidade. TotalFill BC Sealer e AH Plus produziram maiores reduções na contagem microbiana nas primeiras 24 h em comparação com o Bio-C Sealer. Relevância Clínica: 2c.