Properties of Oak Roundwood with and without Frost Cracks

The aim of this study was to examine certain properties of sessile oak wood (Quercus petraea (Matt.) Liebl.) with frost cracks, such as density (&rho
), modulus of rupture (MOR), modulus of elasticity (MOE), and compressive strength in all anatomical directions and to compare it with control trees without frost cracks. Oak with frost cracks had a higher wood density (&rho
= 765 kg &times
m&minus
3) than the control (&rho
= 650 kg &times
3). However, despite its lower density, the control oak was characterized by noticeably better mechanical parameters, with the exception of the compressive strength in radial and tangential directions. Differences in mechanical parameters reached up to 26%. The tests were performed on wood taken from trees with frost cracks that formed over 10 years to several decades ago. Frost cracks can render wood vulnerable to fungi growth, which leads to rotting and discoloration. Differences in strength were found on samples with no visible signs of decay, as they were cut at a distance from the crack. Nonetheless, the observed differences in strength allowed us to conclude that the shreds of fungi, as well as decay, may occur in the entire volume of the frost-damaged log. Such wood is, therefore, of a lower quality than that made of logs without any frost damage. Trees with frost cracks should be progressively be felled during the periodic intermediate cutting, as their wood quality may systematically deteriorate over the years.