Effects of Step-Wise Acid Leaching with HCl on Synthesis of Zeolitic Materials from Paper Sludge Ash

Incinerated ash with a relatively high Ca content, paper sludge ash, was converted to zeolitic materials with high cation-exchange capacities (CECs) by aging at 80 &deg
C in NaOH solution via step-wise acid leaching with HCl to reduce the ash Ca content. The extraction of Ca, Mg, Si, and Al from the ash into the acid solutions during leaching and the products obtained from the leached ash by reaction with an alkali were examined. The contents of Ca and Mg in the ash were more easily extracted from the ash than those of Si and Al in the initial leaching. The leachant pH decreased with increasing numbers of leaching steps, and the amounts of Si, Al, and Ca extracted from the ash increased as a result of the dissolution of gehlenite (Ca2Al2SiO7), one of the main minerals in the ash. Zeolites A and P were synthesized from the leached ashes, and hydroxysodalite was synthesized from the raw ash. With increasing numbers of leaching steps of the ash, the obtained product contained lower released Ca, whereas the product contained higher released Na and has higher CEC, depending on the zeolite phases in the product. The product with the highest CEC was synthesized from third-leached ash, and its CEC was 1.5 mmol/g, which is about four times higher than that of the raw ash (0.4 mmol/g).