Utjecaj termocikliranja na čvrstoću savijanja poliamidne baze proteze

Svrha: Svrha ovoga rada bila je procijeniti utjecaj termocikliranja na čvrstoću savijanja poliamidnog materijala za bazu proteze. Materijali i metode: Testiran je poliamidni protezni materijal (Valplast), a kao kontrola korišten je PMMA (Vertex). Trideset primjeraka svakog materijala izrađeno je za ispitivanje čvrstoće savijanja prema standardu ISO 1567. Svi su uzorci pripremljeni i čuvani 48 sati u vodi na temperaturi od 37 °C, a zatim su podijeljeni u tri jednake skupine (n = 10). Ispitivanje čvrstoće savijanja obavljeno je odmah nakon uranjanja u vodu te nakon termocikliranja (5 °C/55 °C, 2c/min.) poslije 3000 i 5000 ciklusa. Ispitivanje fleksibilnosti provedeno je na trima točkama u univerzalnom stroju za testiranje na brzini križanja od 5 mm/min. Konačna čvrstoća savijanja izračunata je formulom: FS = 3PL/2bd2. Dvosmjerna ANOVA s Tukeyjevim post hoc testom primijenjena je na razini .05 statističke značajnosti. Rezultati: tatistički značajno smanjenje čvrstoće savijanja zabilježeno je nakon termocikliranja poslije 3000 ciklusa za PMMA-e i 5000 ciklusa za oba materijala. Čvrstoća savijanja PMMA-e bila je značajno veća u odnosu na poliamid za sve ispitane uvjete (p < 0,05). Zaključak: Termocikliranje je vrlo nepovoljno djelovalo na čvrstoću savijanja materijala poliamida i materijala PMMA za bazu proteze.
Objective: The aim of the present study was to evaluate the influence of thermocycling on the flexural strength of a polyamide base denture material. Materials and methods: A polyamide denture base material (Valplast) was tested, whereas a PMMA material (Vertex) was used as a control. Thirty specimens of each material were fabricated for flexural strength testing according to ISO 1567. They were prepared and stored in water at 37°C for 48 hours. The specimens of each material were divided into three equal groups (n=10). Flexural strength testing was performed immediately after water storage and after thermocycling (5°C / 55°C, 2 c/min) for 3000 and 5000 cycles. A three point flexural test was performed on a universal testing machine at a crosshead speed of 5 mm/min. The final flexural strength was calculated using the formula: FS = 3 PL/2 bd2. A two-way ANOVA with post-hoc analysis using Tukey’s procedure was applied at .05 level of statistical significance. Results: A statistically significant reduction in flexural strength was recorded after thermocycling at 3000 cycles for PMMA and at 5000 cycles for both materials. The flexural strength of PMMA was significantly higher compared to polyamide for all the conditions tested (p