Luminescence Properties and Decay Kinetics of Mn2+ and Eu3+ Co-Dopant Ions In MgGa2O4 Ceramics

A. Luchechko gratefully acknowledges a grant from the Institute of Physics PAS for a research visit to the institute, while A.I. Popov has been supported by project LZP-2018/1-0214 from the Latvian Council of Science.
The MgGa 2 O 4 ceramics co-doped with Mn 2+ and Eu 3+ ions were synthesized via a higherature solid-state reaction technique. The samples with various Eu 3+ concentrations were characterised using high-resolution photoluminescence (PL) spectroscopy. The PL spectra show weak matrix emission in a blue spectral region with dominant excitation band around 380 nm. Manganese ions are highly excited deeply in UV region and exhibit emission band peaked at 502 nm. The Eu 3+ ions show characteristic f-f excitation and emission lines. The energy transfer between host defects and activator ions was observed. Luminescence decay curves of Mn 2+ and Eu 3+ emission showed complex kinetics with both Eu 3+ -ion concentration and excitation wavelength changes.
Latvian Council of Science LZP-2018/1-0214; Latvian–Ukrainian Joint Research Project LV-UA/2016/1,M/.8-2018; project DB/RIDER0117U004443; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART²