Impact of high-speed sintering and choice of preshaded monochrome or multilayered blanks on fatigue behavior of 4 mol% yttria-stabilized tetragonal zirconia polycrystal

High-speed sintering allows the rapid fabrication of esthetic restorations with adequate flexural strength. However, data on the fatigue behavior of high-speed sintered 4 mol% yttria-stabilized tetragonal zirconia polycrystal (4Y-TZP) are lacking.The purpose of this in vitro study was to examine the effect of high-speed sintering and the preshading of blanks (monochrome versus multilayer) on the fatigue behavior of 4Y-TZP ceramics.Four-point flexural strength specimens (N=405) were fabricated from high-speed sintered multilayer 4Y-TZP (Zolid DRS) processed at 1580 °C for about 20 minutes and conventionally sintered at 1450 °C for about 10 hours, multilayer 4Y-TZP (Zolid Gen-x), and monochrome 4Y-TZP (Ceramill Zolid HT+PS), the control group. The specimens were loaded under 5 different dynamic test conditions for fatigue testing (P1-P5). Three were step-stress protocols (P1: 50 N for 5000 cycles; P2: 10 N for 1000 cycles, P3: 5% for 5000 cycles), 1 was tested with a constant force of 720 N (P4), and 1 was tested for different constant load levels (P5). For analysis of P1-P3, the Kaplan-Meier test and Mantel Cox test were performed (α=.05). P4 was analyzed with the Kolmogorov-Smirnov, Kruskal-Wallis, and Mann-Whitney U tests, and P5 by creating a load-cycle diagram. A fracture analysis was performed.ZMLC showed better fatigue behavior than ZMLH (P≤.006) and ZMOC (P≤.002) in all 3 step-stress protocols (P1-P3). ZMLH showed results comparable with those for ZMOC (P≥.285). In P4 and P5, all materials showed comparable values (P=.163 for P4).The multilayer technique showed a positive effect on the fatigue behavior of 4Y-TZP. In contrast, high-speed sintering negatively influenced the fatigue behavior of multilayer 4Y-TZP. The high-speed sintered material showed no deterioration compared with the conventional sintered monochrome material.