Influencia de los parámetros de soldeo fuerte en la microestructura y propiedades mecánicas de la unión de la aleación base níquel Hastelloy B2

A study of the high vacuum brazing process of solid solution strengthened Hastelloy B2 nickel alloy has been done. A first stage of research has focused on the selection of the most appropriate brazing filler metal to the base material and vacuum furnace brazing process. The influence of welding parameters on joint microstructure constituents, relating the microstructure of the joint to its mechanical properties, has been evaluated. Two gaps of 50 and 200 micrometers, and two dwell times at brazing temperature of 10 and 90 minutes were studied. The braze joint mainly consists of the nickel rich matrix, nickel silicide and ternary compounds. Finally, the results of this study have shown the high bond strength for small gaps and increased dwell times of 90 minutes.Se realizó un estudio pormenorizado del proceso de soldeo fuerte en horno de alto vacío de la aleación base níquel Hastelloy B2 fortalecida por solución sólida. En una primera fase del trabajo se seleccionó el material de aporte acorde al material objeto de unión y a la fuente de calentamiento seleccionada. Posteriormente, se evaluó la influencia del gap (50 y 200 micrómetros) y tiempo de permanencia a temperatura de soldeo (10 y 90 minutos) sobre los microconstituyentes de la unión, relacionando la microestructura con las propiedades mecánicas de la junta. Los análisis metalográficos mostraron una unión constituida por una matriz rica en níquel, siliciuros de níquel y compuestos ternarios. Finalmente, los resultados de los ensayos mecánicos a esfuerzos cortantes mostraron una elevada resistencia para gaps de 50 micrómetros y tiempos de permanencia de 90 minutos.