Molybdate-Tellurite Compounds with Capped-Kagomé Spin-Lattices

Three new molybdate-tellurites, K2M9(TeO3)4(MoO4)4(OH)4 (M = NiII and CoII) and (NH4)2Cu9II(TeO3)4(MoO4)4(OH)4, have been successfully synthesized by conventional hydrothermal method. Due to the influence of the Jahn-Teller effect, these compounds crystallize in different space groups of rhombohedral R3m, monoclinic P21/c and triclinic P1 for Ni-, Co-, and Cu-analogues, respectively. The topological arrangements of magnetic ions in these compounds show that deficient capped-kagome spin-lattices with kagome positions exhibit different 1/6 depletion. Magnetic and specific heat measurements confirm that K2Ni9(TeO3)4(MoO4)4(OH)4 exhibits a spin-glass behavior at low temperature, while (NH4)2Cu9(TeO3)4(MoO4)4(OH)4 possesses a long-range canted antiferromagnetic ordering with TN ∼ 10.8 K and further shows a 3/5 magnetization plateau in the magnetization curve at low temperature.