Cytotoxicity, cytoprotection and morphological analysis of MTA, MTA Repair HP and Biodentine

The aim of the present study was to evaluate the in vitro cytotoxicity, cytoprotection and morphological changes by SEM technique of MTA, MTA-HP and Biodentine, on fibroblast 3T3 cell line. MTA, MTA-HP, and Biodentine were disposed into teflon sterile discs and incubated in culture media for 24 hours to obtain elutes. Fibroblast 3T3 cells were cultured with the respective elutes and control group with culture medium. Cytotoxicity and cytoprotection assays were determined by MTT method. The results were statistically processed by Mann-Whitney (α=0.05) and Kruskal-Wallis analysis. Cells cultured in coverslips and treated with the elutes were submitted to fixation and dehydration process to evaluate morphological alterations by SEM technique. In cytotoxicity assay, cells treated with MTA, MTA HP and Biodentine showed viability above 95%, like control cells. In cytoprotection to the 3T3 cells, materials promoted at the same magnitude (p>0.05), with improved cell growth and were considered statistically different from the obtained for cells only treated with peroxide solution (positive control) (p=0.046). Also, viability results of the tested root canal materials were close to that of the negative control (cells treated only with culture medium) (p=0.05). No morphologic cell changes of 3T3 cells in contact with the endodontic materials were revealed by SEM technique. The bioceramic materials has demonstrated high bioactivity and biocompatibility, as presented in cytoprotection and morphological trials. El objetivo del presente estudio fue evaluar la citotoxicidad, citoprotección y cambios morfológicos in vitro por técnica SEM de MTA, MTA-HP y Biodentine, en la líneo celular de fibroblastos 3T3. MTA, MTA-HP y Biodentine se colocaron en discos estériles de teflón y se incubaron en medios de cultivo durante 24 horas para obtener eluidos. Las células de fibroblastos 3T3 se cultivaron con los eluidos respectivos y el grupo de control con medio de cultivo. Los ensayos de citotoxicidad y citoprotección se determinaron mediante el método MTT. Los resultados fueron procesados estadísticamente por Mann-Whitney (α=0,05) y análisis de Kruskal-Wallis. Las células cultivadas en cubreobjetos y tratadas con los eluidos fueron sometidas a proceso de fijación y deshidratación para evaluar alteraciones morfológicas por técnica SEM. En el ensayo de citotoxicidad, las células tratadas con MTA, MTA HP y Biodentine mostraron una viabilidad superior al 95 %, al igual que las células de control. En la citoprotección a las células 3T3, los materiales promovieron en la misma magnitud (p>0.05), con crecimiento celular mejorado y se consideraron estadísticamente diferentes a los obtenidos para las células tratadas únicamente con solución de peróxido (control positivo) (p=0.046). Además, los resultados de viabilidad de los materiales del conducto radicular probados fueron similares a los del control negativo (células tratadas solo con medio de cultivo) (p = 0,05). La técnica SEM no reveló cambios celulares morfológicos de las células 3T3 en contacto con los materiales endodónticos. Los materiales biocerámicos han demostrado una alta bioactividad y biocompatibilidad, tal como se presenta en los ensayos de citoprotección y morfológicos. O objetivo do presente estudo foi avaliar a citotoxicidade in vitro, citoproteção e alterações morfológicas pela técnica de MEV do MTA, MTA-HP e Biodentine, na linhagem celular de fibroblastos 3T3. MTA, MTA-HP e Biodentine foram dispostos em discos estéreis de teflon e incubados em meio de cultura por 24 horas para obtenção dos eluatos. Células de fibroblastos 3T3 foram cultivadas com os respectivos eluatos e o grupo controle com meio de cultura. Os ensaios de citotoxicidade e citoproteção foram determinados pelo método MTT. Os resultados foram processados ​​estatisticamente pela análise de Mann-Whitney (α=0,05) e Kruskal-Wallis. As células cultivadas em lamínulas e tratadas com os eluatos foram submetidas ao processo de fixação e desidratação para avaliação das alterações morfológicas pela técnica de MEV. No ensaio de citotoxicidade, as células tratadas com MTA, MTA HP e Biodentine apresentaram viabilidade acima de 95%, assim como as células controle. Na citoproteção das células 3T3, os materiais promoveram na mesma magnitude (p>0,05), com melhor crescimento celular e foram considerados estatisticamente diferentes do obtido para células tratadas apenas com solução de peróxido (controle positivo) (p=0,046). Além disso, os resultados de viabilidade dos materiais endodônticos testados foram próximos aos do controle negativo (células tratadas apenas com meio de cultura) (p=0,05). Nenhuma alteração morfológica das células 3T3 em contato com os materiais endodônticos foi revelada pela técnica de MEV. Os materiais biocerâmicos demonstraram alta bioatividade e biocompatibilidade, conforme apresentado em ensaios de citoproteção e morfológicos.