Determination of copolymer ratios of poly(lactide-co-glycolide) using near-infrared spectroscopy

The near infrared (NIR) spectroscopic technique was used to determine copolymer ratios of polylactide-co-glycolide samples. Appropriate quantities of dl -polylactic acid and lactic-co-glycolic acid polymers with 86:14, 75:25, 64:36 and 52:48 lactide to glycolide ratios were dissolved in methylene chloride to obtain 5% (w/w) solutions. NIR spectra of the samples were obtained from the solutions using a Polyol Analyzer™ operated in the transmittance mode. Linear regression calibration models were generated at 2130 and 2288 nm from the second derivative spectral data obtained from the NIR technique. The lowest and highest standard errors of calibration (SEC) at 2130 nm were 1.29 and 1.63%, whereas those obtained from the calibration models generated at 2288 nm were 2.00 and 2.03%, respectively. Partial least squares (PLS) calibration models were also generated from the second derivative spectral data from 1100 to 2500 nm. The lowest and the highest SEC for the models were 1.46 and 1.53%, respectively. The calibration models were then used to predict the lactide contents of the unknown (test) samples. The highest percent error of prediction was 2.56% for samples with 86% lactide content when the linear regression calibration at 2130 nm was used, whereas the highest percent error of prediction was 1.56% for samples with 64% lactide content when the linear regression calibration at 2288 nm was used. The highest percent error of prediction was 1.73% for samples with 75% lactide content when the two-factor PLS calibration model was used.