High-Strength Regenerated Cellulose Fiber Reinforced with Cellulose Nanofibril and Nanosilica

In this study, a novel type of high-strength regenerated cellulose composite fiber reinforced with cellulose nanofibrils (CNFs) and nanosilica (nano-SiO2) was prepared. Adding 1% CNF and 1% nano-SiO2 to pulp/AMIMCl improved the tensile strength of the composite cellulose by 47.46%. The surface of the regenerated fiber exhibited a scaly structure with pores, which could be reduced by adding CNF and nano-SiO2, resulting in the enhancement of physical strength of regenerated fibers. The cellulose/AMIMCl mixture with or without the addition of nanomaterials performed as shear thinning fluids, also known as “pseudoplastic” fluids. Increasing the temperature lowered the viscosity. The yield stress and viscosity sequences were as follows: RCF-CNF2 &gt
RCF-CNF2-SiO22 &gt
RCF-SiO22 &gt
RCF &gt
RCF-CNF1-SiO21. Under the same oscillation frequency, G’ and G” decreased with the increase of temperature, which indicated a reduction in viscoelasticity. A preferred cellulose/AMIMCl mixture was obtained with the addition of 1% CNF and 1% nano-SiO2, by which the viscosity and shear stress of the adhesive were significantly reduced at 80 °C.