Injectable PLGA microsphere/calcium phosphate cements: physical properties and degradation characteristics

Contains fulltext : 50853.pdf (Publisher’s version ) (Closed access) Calcium phosphate (CaP) cements show an excellent biocompatibility and often have a high mechanical strength, but in general degrade relatively slow. To increase degradation rates, macropores can be introduced into the cement, e.g., by the inclusion of biodegradable microspheres into the cement. The aim of this research is to develop an injectable PLGA microsphere/CaP cement with sufficient setting/cohesive properties and good mechanical and physical properties. PLGA microspheres were prepared using a water-in-oil-in-water double-emulsion technique. The CaP-cement used was Calcibon, a commercially available hydroxyapatite-based cement. 10:90 and 20:80 dry wt% PLGA microsphere/CaP cylindrical scaffolds were prepared as well as microporous cement (reference material). Injectability, setting time, cohesive properties and porosity were determined. Also, a 12-week degradation study in PBS (37 degree C) was performed. Results showed that injectability decreased with an increase in PLGA microsphere content. Initial and final setting time of the PLGA/CaP samples was higher than the microporous sample. Porosity of the different formulations was 40.8% (microporous), 60.2% (10:90) and 69.3% (20:80). The degradation study showed distinct mass loss and a pH decrease of the surrounding medium starting from week 6 with the 10:90 and 20:80 formulations, indicating PLGA erosion. Compression strength of the PLGA microsphere/CaP samples decreased siginificantly in time, the microporous sample remained constant. After 12 weeks both PLGA/CaP samples showed a structure of spherical micropores and had a compressive strength of 12.2 MPa (10:90) and 4.3 MPa (20:80). Signs of cement degradation were also found with the 20:80 formulation. In conclusion, all physical parameters were well within workable ranges with both 10:90 and 20:80 PLGA microsphere/CaP cements. After 12 weeks the PLGA was totally degraded and a highly porous, but strong scaffold remained.