Melioration of Electrical and Optical Properties of Al and B Co-Doped ZnO Transparent Semiconductor Thin Films

Undoped, Al-doped and Al-B co-doped ZnO transparent semiconductor thin films were deposited on glass substrates by sol-gel method and spin coating technique. This study investigated the influence of Al (2 at.%) doping and Al (2 at.%)-B (1 or 2 at.%) co-doping on the microstructural, surface morphological, electrical and optical properties of the ZnO-based thin films. XRD analysis indicated that all as-prepared ZnO-based thin films were polycrystalline with a single-phase hexagonal wurtzite structure. The substitution of extrinsic dopants (Al or Al-B) into ZnO thin films can significantly degrade the crystallinity, refine the microstructures, improve surface flatness, enhance the optical transparency in the visible spectrum and lead to a shift in the absorption edge toward the short-wavelength direction. Experimental results showed that the Al-doped and Al-B co-doped ZnO thin films exhibited high average transmittance (&gt
91.3%) and low average reflectance (&lt
10%) in the visible region compared with the ZnO thin film. The optical parameters, including the optical bandgap, Urbach energy, extinction coefficient and refractive index, changed with the extrinsic doping level. Measured results of electrical properties revealed that the singly doped and co-doped samples exhibited higher electron concentrations and lower resistivities than those of the undoped sample and suggested that 2 at.% Al and 1 at.% B were the optimum dopant concentrations for achieving the best electrical properties in this study.