Curing, Monomer Leaching and Water Sorption of TEGDMA/BisGMA Photopolymerized Copolymers

The aim of this work was to correlate the degree of conversion with residual monomer release and water absorption of 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy) phenyl]propane (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA) (TB copolymers) obtained by photopolymerization, using canforquinone/ethyl 4-dimethylaminobenzoate (CQ/EDB) photoinitiator. The monomer release from the copolymers was evaluated by immersion in ethanol/water and HPLC (high performance liquid chromatography) analysis. Water absorption from artificial saliva was determined by mass variation. The results show that the composition of the TB copolymers influences the polymerization kinetics, the amount of the released monomers, the degree of conversion and the amount of adsorbed water. A clear correlation can be found between these properties. O objetivo deste trabalho é correlacionar o grau de conversão de copolímeros de 2,2-bis[4-(2-hidróxi-3-metacriloiloxipropóxi) fenil]propano (BisGMA) e dimetacrilato de trietilenoglicol (TEGDMA) (copolímeros TB) obtidos por fotopolimerização, usando o sistema fotoiniciador canforquinona/etil 4-dimetilaminobenzoato (CQ/EDB), com a eluição de monômeros e a absorção de água. A eluição de monômeros foi avaliada a partir da imersão dos polímeros em etanol/água e análise por CLAE (cromatografia líquida de alto rendimento). A absorção de água de saliva artificial foi determinada gravimetricamente. Os resultados mostram que a composição dos copolímeros TB influencia a cinética de polimerização, a quantidade de monômeros eluídos, o grau de conversão e a quantidade de água adsorvida. Uma boa correlação foi encontrada entre estas propriedades.