XPS investigations on cesium uranates : mixed valency behaviour of uranium'

Several pure cesium uranate phases were prepared (Cs 2 U 2 O 7 , Cs 2 U 4 O 13 , Cs 2 U 4 O 12 , Cs 4 U 5 O 17 ) and measured with X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Detailed XPS scans of the main photoelectron peaks (U 4f, Cs 3d, O 1s and valence band) were made. Peak positions, peak widths and satellite positions were measured and compared between the uranates. A systematic shift in the position of the U 4f lines was found to be correlated with the Cs/U ratio. The mixed valency behaviour of uranium was observed and studied. Interpretation of the satellite structure of the U 4f peaks and the deconvolution of these peaks have been used to quantify the chemical states of uranium present in the mixed valency compound Cs 2 U 4 O 12 .