Structural, optical and vibrational properties of ZnO:M (M=Al3+ and Sr2+) nano and micropowders grown by hydrothermal synthesis

Powders of ZnO and ZnO:M (M = Al3+ and Sr2+) with 1 and 4% of M nominal content were synthetized by a hydrothermal method in a diethanolamine (DEA) medium. The samples were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), micro-Raman and photoluminescence (PL). The powder particles were spherical with average radius decreasing from 1 μm down to 70 nm with increasing Al3+ nominal content but nearly independent on the Sr2+ nominal content. The XRD and micro-Raman results indicate that both Al3+ and Sr2+ mostly incorporated substitutionally into the ZnO lattice, giving rise to compressive and tensile strain, respectively, as a result of ionic radii differences. The PL spectra for ZnO:Al exhibit a dopant-induced contribution at ∼3.1 eV, which is not observed for ZnO:Sr, due to radiative transitions involving trapping of photocarriers at theoretically expected substitutional Al3+ donor states or at Zn interstitial defects. Fil: Marín Ramírez, Oscar Alonso. Universidad Nacional de Tucumán. Instituto de Física del Noroeste Argentino. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet Noa Sur. Instituto de Física del Noroeste Argentino; Argentina. Universidad Nacional de Tucumán. Facultad de Ciencias Exactas y Tecnología. Laboratorio de Física del Sólido; Argentina Fil: Soliz, Tania. Universidad Nacional de Tucumán. Facultad de Ciencias Exactas y Tecnología; Argentina Fil: Gutierrez, Jorge Andrés. Universidad del Quindío. Facultad de Ciencias Básicas y Tecnológicas; Colombia Fil: Tirado, Monica Cecilia. Universidad Nacional de Tucumán. Instituto de Física del Noroeste Argentino. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet Noa Sur. Instituto de Física del Noroeste Argentino; Argentina. Universidad Nacional de Tucumán. Facultad de Ciencias Exactas y Tecnología. Departamento de Física. Departamento de Nanomateriales y Propiedades Dieléctricas; Argentina Fil: Figueroa, Carlos. Universidad Nacional de Tucumán. Instituto de Física del Noroeste Argentino. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet Noa Sur. Instituto de Física del Noroeste Argentino; Argentina. Universidad Nacional de Tucumán. Facultad de Ciencias Exactas y Tecnología. Laboratorio de Física del Sólido; Argentina Fil: Comedi, David Mario. Universidad Nacional de Tucumán. Instituto de Física del Noroeste Argentino. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet Noa Sur. Instituto de Física del Noroeste Argentino; Argentina. Universidad Nacional de Tucumán. Facultad de Ciencias Exactas y Tecnología. Laboratorio de Física del Sólido; Argentina