Preparations of NiFe2O4 Yolk-Shell@C Nanospheres and Their Performances as Anode Materials for Lithium-Ion Batteries

At present, lithium-ion batteries (LIBs) have received widespread attention as substantial energy storage devices
thus, their electrochemical performances must be continuously researched and improved. In this paper, we demonstrate a simple self-template solvothermal method combined with annealing for the synthesis of NiFe2O4 yolk-shell (NFO-YS) and NiFe2O4 solid (NFO-S) nanospheres by controlling the heating rate and coating them with a carbon layer on the surface via high-temperature carbonization of resorcinol and formaldehyde resin. Among them, NFO-YS@C has an obvious yolk-shell structure, with a core-shell spacing of about 60 nm, and the thicknesses of the NiFe2O4 shell and carbon shell are approximately 15 and 30 nm, respectively. The yolk-shell structure can alleviate volume changes and shorten the ion/electron diffusion path, while the carbon shell can improve conductivity. Therefore, NFO-YS@C nanospheres as the anode materials of LIBs show a high initial capacity of 1087.1 mA h g&minus
1 at 100 mA g&minus
1, and the capacity of NFO-YS@C nanospheres impressively remains at 1023.5 mA h g&minus
1 after 200 cycles at 200 mA g&minus
1. The electrochemical performance of NFO-YS@C is significantly beyond NFO-S@C, which proves that the carbon coating and yolk-shell structure have good stability and excellent electron transport ability.