Growth and basic dielectric data of high quality TSCC crystals

Tris-sarcosine calcium chloride (TSCC) single crystals were grown from water solutions by the isothermal evaporation method. The growth solutions contained sarcosine and CaCl2 either in stoichiometric or nonstoichiometric ratio. The required phase diagram sarcosine–CaCl2H2O at 40 °C was determined by the synthetic method. PFT 400 MHz NMR was used for the analysis of organic impurities in sarcosine and TSCC. The crystals grown from both types of solutions had maximum values of the dielectric permittivity 10 to 200 times larger than those measured by other authors at comparable measuring frequencies and fields. It is discussed in terms of crystal quality. Trisarcosin-Calciumchlorid (TSCC) Einkristalle wurden nach der Methode der isothermen Verdampfung aus wasrigen Losungen gezuchtet. Die Zuchtungslosungen enthielten Sarcosin und CaCl2 in stochiometrischer oder nichtstochiometrischer Zusammensetzung. Das Phasendiagramm Sarcosin–CaCl2H2O wurde bei 40 °C nach der synthetischen Methode bestimmt. Puls-Fourier-Transform NMR bei 400 MHz wurde zur Analyse organischer Verunreinigungen in Sarcosin und TSCC benutzt. Die Kristalle aus beiden Arten von Losungen hatten Maximalwerte der Dielektrizitatskonstanten, die um den Faktor 10 bis 200 groser waren, als sie von anderen Autoren bei vergleichbaren Mesfrequenzen und Feldern gemessen wurden. Dies wird im Zusammenhang mit der Kristallqualitat diskutiert.