Properties of magnetically diluted nanocrystals prepared by mechanochemical route

The bulk and surface properties of magnetically diluted Cd 0.6 Mn 0.4 S nanocrystals synthesized by solid state route in a planetary mill were studied. XRD, SEM, TEM (HRTEM), low-temperature N 2 sorption, nanoparticle size distribution as well as SQUID magnetometry methods have been applied. The measurements identified the aggregates of small nanocrystals, 5–10 nm in size. The homogeneity of produced particles with well developed specific surface area (15–66 m 2 g −1 ) was documented. The transition from the paramagnetic to the spin-glass-like phase has been observed below ∼40 K. The changes in the magnetic behaviour at low temperatures seem to be correlated with the formation of the new surface area as a consequence of milling. The magnetically diluted Cd 0.6 Mn 0.4 S nanocrystals are obtained in the simple synthesis step, making the process attractive for industrial applications.