Nd/V Co-Doped Bi4Ti3O12Powder Prepared By Molten Salt Synthesis

Powders of Nd/V-doped Bi4Ti3O12 with a composition Bi3.74Nd0.26Ti2.98V0.02O12.01 (BNTV), prepared by the molten salt synthesis, using chlorides as the fluxes, were successfully obtained. The influences of the molar ratio of KCl to NaCl, temperature, and soak time on the formation and morphology of BNTV were investigated. The results indicated that Na+ can enter the lattice of Bi4Ti3O12 (BIT), leading to a decrease in the cell dimensions of BIT phase. The grain size and morphology of BNTV powders were considerably affected by the molar ratio of KCl to NaCl in the fluxes, in which the platelets showed the morphology of a rectangle and no regular shape in KCl and NaCl fluxes, respectively. The grain size of BNTV increased with increasing amount of NaCl in the fluxes, but the thickness decreased. The platelets prepared in the NaCl flux were faceted along (0 0 1) plane.