Spin glass behavior in some Fe–Mn–Al disordered alloys

In this work, we report an ac susceptibility study of Fe0.5Mn0.2Al0.3, Fe0.5Mn0.1Al0.4, and Fe0.225Mn0.375Al0.40 disordered alloys. All the samples exhibit only one well defined peak near 58, 18, and 31 K, respectively. When the frequency of the ac field increases, the measured intensities of the peaks decrease and the maxima shift to higher temperatures, and when the dc field increases the intensity of the peaks decreases. This dependence of the position and intensity of the peaks on the field and frequency is evidence of the spin glass character of the transitions in these alloys. Mossbauer spectra at different temperatures were performed for the sample with 30 at. % Al and the plot of the adjusted mean hyperfine field versus temperature shows a kink at 53 K which is further evidence that this sample shows spin glass behavior.