On the melting behaviour of isotactic polymers obtained from optically active and racemic 4-methyl-1-hexene

The thermal behaviour of isotactic poly[(S)-4-methyl-1-hexene], (P(S)4 MH), isotactic poly[(R)-4-methyl-1-hexene], (P(R)4 MH), of their equimolar mixture (r-P4MH) and of poly[(R)(S)-4-methyl-1-hexene], (P4MH), was investigated. The DSC curves obtained by melting P(S)4MH and P(R)4MH showed two endothermic peaks, while only one peak was found in the DSC curves obtained by melting r-P4MH or P4MH. For the optically active polymers the formation of a mesophase is proposed and the results are discussed on the basis of the conformation of these polymers in the crystalline and in the liquid state. Das thermische Verhalten von isotaktischem Poly[(S)-4-methyl-1-hexen], (P(S)4MH), Poly[(R)-4-methyl-1-hexen], (P(R)4MH), ihrer aquimolaren Mischung (r-P4MH) und von Poly[(R)(S)-4-methyl-1-hexen] (P4MH) wurde untersucht. Die DSC-Kurven von P(S)4MH und P(R)4MH ergaben beim Schmelzen zwei endotherme Peaks, wahrend nur ein Peak in den DSC-Kurven von r-P4MH und P4MH gefunden wurde. Fur die optisch aktiven Polymeren wird die Bildung einer Mesophase vorgeschlagen und die experimentellen Ergebnisse werden auf der Basis der Konformation dieser Polymeren im kristallinen und flussigen Zustand besprochen.