Refinement of the Superstructure of C-Type Gallium Tris(metaphosphate), Ga(PO3)3

Single crystals of Ga(PO3)3 were grown in polyphosphoric acid melts by heating a mixture of Ga2O3 and H3PO4 (350 °C, 7 d). The compound belongs to the series of metaphosphates MIII(PO3)3 forming the C-type structure (monclinic, Cc, Z = 12, a = 13.0058(21), b = 18.915(3), c = 9.3105(15) A, β = 126.900(11), 5348 independent reflections (I > 0); 354 variables; 39 atoms in asymetric unit; R1 = 0.048, wR2 = 0.1034). The structure is characterized by a superstructure with tripled monoclinic b-axis. Three crystallographically independent GaIIIO6 octahedra (d¯(Ga–O) = 1.950 A) are linked by 1∞(PO3)– chains. Verfeinerung der Uberstruktur von C-Typ Gallium-tris(metaphosphat) Einkristalle von Ga(PO3)3 wurden in Polyphosphorsaureschmelzen aus Ga2O3 und H3PO4 gezuchtet (620 K, 7 d). Die Verbindung gehort zu einer Serie von Metaphosphaten MIII(PO3)3, welche den sogenannten C-Strukturtyp (z. B.: C–Al(PO3)3) ausbilden. Charakteristisches Strukturmerkmal ist eine Uberstruktur mit Verdreifachung der monoklinen b-Achse. Drei kristallographisch unabhangige GaIIIO6 Oktaeder (d¯(Ga–O) = 1.950 A) werden durch 1∞(PO3)– verknupft.