Thickness-Dependent Evolution of Piezoresponses and Stripe 90° Domains in (101)-Oriented Ferroelectric PbTiO3 Thin Films

High-index ferroelectric films as (101)-orientated ones exhibit enhanced dielectric responses, piezoelectric responses, and exotic ferroelectric switching behaviors, which are potential candidates for applications in memories and capacitors. However, possible domain patterns and domain wall structures in (101)-oriented ferroelectric thin films are still elusive, which results in difficulties in understanding the origin and further modulating their special properties. In this work, a series of PbTiO3 (PTO) thin films with 35, 50, 60, and 70 nm in thickness were grown on (101)-oriented (LaAlO3)0.29(SrTa1/2Al1/2O3)0.71 (LSAT(101)) substrates by pulsed laser deposition and investigated by both piezoresponse force microscopy (PFM) and (scanning) transmission electron microscopy ((S)TEM). PFM measurements reveal that periodic stripe domains are dominant in 50 nm thick PTO films. Besides stripe domains, a/c domains appear in films with thickness more than 60 nm. A thickness-dependent evolution of piezoresponse a...