Influence of hydrogen on dwell-fatigue response of near-alpha titanium alloys

The prior studies have investigated the influence of internal hydrogen on dwell-fatigue behavior of near-α titanium alloys primarily in the lamellar microstructural condition. In the current study, the effects of internal hydrogen, in the range 10–230 ppm (by weight), on the dwell-fatigue behavior of Ti-6242Si alloy were investigated. The examined alloy had a bimodal microstructure comprising approximately 70 vol% primary α grains and 30 vol% transformed β regions. The dwell-fatigue life generally increased with increasing hydrogen content. The dwell-fatigue lives were longer by a factor of as high as 6 for high (≥150 ppm) hydrogen contents than for the low ( 150 ppm) hydrogen contents. Specifically, these facets were inclined at ∼8 – 17° from the basal plane. Therefore, the longer dwell-fatigue lives observed for the alloys with hydrogen contents ≥150 ppm could not be explained on the basis of any differences in crystallography of the facets at crack-initiation sites. The longer dwell-fatigue lives for higher hydrogen contents can be explained within the framework of time-dependent load shedding from the soft microtextured regions (MTRs) to the hard MTRs if the local stress redistribution at the soft MTR/hard MTR boundary due to the hold at maximum load is reduced with increasing hydrogen content.