Effect of post-annealing on the magnetic properties of sputtered Mn56Al44 thin films

Mn56Al44 (MnAl) thin films of constant thickness (∼30nm) were grown on naturally oxidized Si substrates using DC-magnetron sputtering. Effect of deposition parameters such as sputtering power, substrate temperature (Ts), and post-annealing temperature have been systematically invstigated. X-ray diffraction patterns revealed the presence of mixed phases, namely the τ- and β-MnAl. The highest saturation magnetization (MS) was found to be 65emu/cc using PPMS-VSM in film grown at Ts=500°C. The magnetic ordering was found to get significantly improved by performing post-annealing of these as-grwon at 400°C for 1 hr in the presence of out-of-plane magnetic field of ∼1500Oe in vacuum. In particular, at room temperature (RT), the MS got enhanced after magnetic annealing from 65emu/cc to 500 emu/cc in MnAl films grown at Ts=500°C. This sample exhibited a magneto-resistance of ∼1.5% at RT. The tuning of the structural and magnetic properties of MnAl binary alloy thin films as established here by varying the growth parameters is critical with regards to the prospective applications of MnAl, a metastable ferromagnetic system which possesses the highest perpendicular magnetic anisotropy at RT till date.Mn56Al44 (MnAl) thin films of constant thickness (∼30nm) were grown on naturally oxidized Si substrates using DC-magnetron sputtering. Effect of deposition parameters such as sputtering power, substrate temperature (Ts), and post-annealing temperature have been systematically invstigated. X-ray diffraction patterns revealed the presence of mixed phases, namely the τ- and β-MnAl. The highest saturation magnetization (MS) was found to be 65emu/cc using PPMS-VSM in film grown at Ts=500°C. The magnetic ordering was found to get significantly improved by performing post-annealing of these as-grwon at 400°C for 1 hr in the presence of out-of-plane magnetic field of ∼1500Oe in vacuum. In particular, at room temperature (RT), the MS got enhanced after magnetic annealing from 65emu/cc to 500 emu/cc in MnAl films grown at Ts=500°C. This sample exhibited a magneto-resistance of ∼1.5% at RT. The tuning of the structural and magnetic properties of MnAl binary alloy thin films as established here by varying the growth ...