Development of temperature-heating rate diagrams for the pyrolytic removal of binder used for powder injection moulding

A polypropylene-based binder system was used to injection mould test bars containing 65 vol % aluminium powder. Specimens, 3 and 6 mm thick, made from these bars were used for pyrolytic binder removal experiments in static air and nitrogen. The development of a carefully defined experimental procedure for the determination of the heating rate at which binder removal can be carried out at a given temperature without the creation of macro defects is fully described. The use of isothermal heat treatments during pyrolysis are also considered and results are presented as temperature-heating rate diagrams for each atmosphere and thickness investigated. These diagrams show a lower and an upper boundary. Defect formation occurs if the temperature-heating rate relationship lies between the boundaries. Near optimum binder removal schedules deduced from each diagram have been experimentally verified.