Haftfestigkeit eines mit β-Trikalziumphosphat angereichertem Knochenadhäsivs

Background: This investigation describes experimental tests of the biomechanical features of a new resorbable bone adhesive based on methacrylate-terminated oligolactides enhanced with osteoconductive β-tricalcium phosphate. Material and Methods: 51 New Zealand white rabbits were randomised to an adhesive group (n = 29) and a control group (n = 22). An extra-articular bone cylinder was taken from the proximal tibia, two stripes of adhesive were applied and the cylinders were replanted. After 10 and 21 days, 3 and 12 months tibial specimens were harvested and the cylinder pull-out test was performed with a servo-hydraulic machine. Additionally the pull-out force was evaluated with the bone-equivalent Ebazell® after 5, 10 and 360 minutes in 14 specimens each. Results: Average pull-out forces in the adhesive group were 28 N after 10 days (control: 57 N), 155 N after 21 days (216 N), 184 N after 3 months (197 N) and 205 N after 12 months (185 N). Investigations with Ebazell® showed almost identical pull-out forces after 5 min, 15 min and 360 min. Adhesive forces were as high as 125 N/cm2 of adhesive surface and more than 1200 N/g of adhesive mass. Conclusions: The adhesive investigated here has a very good primary adhesive power, compared to the literature data, achieved after only 5 minutes. Even in moist surroundings the adhesive capacity remains sufficient. The adhesive has to prove its resorptive properties in further investigations and in first line its medium-term and long-lasting biocompatibility. Furthermore, biomechanical features will have to be compared to those of conventional fixation techniques.