Studies on the Preparation and DeNOx Performance of MnxOy/CNTs Catalyst for Low-Temperature Selective Catalytic Reduction

The metal oxide catalyst was prepared by loading MnxOyon carbon nanotubes (CNTs) with impregnation method. Then the catalyst was characterized by BET, TEM and XPS, and the catalytic activity of the catalyst for selective catalytic reduction (SCR) of NO at low-temperature was investigated. The results showed that the species of active components loaded on the catalyst were MnO2and Mn2O3. The NO conversion was improved with reduction temperature increase under 250°C, increased slowly over 250°C. The O2content had an outstanding effect on NO conversion of catalysts at a low concentration range. Once the oxygen content was enhanced over 5%, there was no significant increase in the NO conversion. With the increasing of space velocity, the NO conversion rate was decreased under the reaction conditions.