Oxidation Behavior of TiC/Mo Composites by Spark Plasma Sintering

This paper aims to research the high-temperature oxidation behavior of TiC/Mo composite. Adding 5 wt.% TiC, Mo-based composite was prepared by Spark Plasma Sintering. The composite was oxidized at different temperatures (400°C, 600°C, 800°C, 1000°C and 1200°C) and times (5 min, 10 min, 20 min, 30 min and 60 min). When oxidation was at 400-1000°C for 20 minutes, the degree of oxidation intensifies with the increase of temperature, and TiO2 was observed at 1000°C. While the temperature was 1200°C, the oxidation rate gradually decreased with the increase of time. The result shows that the formation of TiO2 can inhibit the oxidation process.