Preparation and electrochemical behavior of amorphous Co-Mo coating with high content of Mo

At present, alloy materials have been widely used as wear-resistant coatings due to good mechanical properties. In this paper, electrodeposition was used to prepare the Co-Mo coating. The electrochemical behavior of the deposition of alloy and the phase composition, morphology, composition and property of the coating have been studied. The study of process parameters found that when the concentration of Na2Mo4 is 0.05mol/L, the concentration of C6H5Na3O7 is 0.15mol/L, the pH of the solution is 7, and the temperature is 50℃, the content of Mo in Co-Mo coating is 39.56%, and the microhardness reaches the maximum value of 503HV. The study of electrochemical behavior found that when the concentration of Na2Mo4 is 0.05mol/L, the concentration of C6H5Na3O7 is 0.15mol/L, the pH of the solution is 7 and the temperature is 50℃, the most positive deposition potential, maximum exchange current density and minimum charge transfer impedance were obtained, which explained why the best performance coating can be obtained under this condition.